交聯劑HOLPOSON® FM-1

由旭硝子株式會社研發的交聯劑FM-1與各種織物拼用結合能賦予高耐久性能，加工布的耐水性。具有多分支多官能末端封閉型異氰酸脂基團，結合拼用織物防水劑經過加熱處理提高交聯性能效果。與織物防水劑等其它弱陽離子及非離子乳液相溶性良好。加熱處理時不會發生甲醛。

一、物化性能

産品型号 原裝進口

外 觀 白色至淡黃色乳液

化學組成 未端封閉異氰酸鈉

離 子 性 弱陽離子型

pH 值 弱酸性

溶 解 性 易稀釋溶于水中

二、使用方法

浸軋法（一浸一軋）

用量： 10 - 20g/L

幹燥條件 110℃ × 1-2分鐘

烘焙條件 170℃ × 1-2分鐘

注意事項

1.因處理條件的不同有變色（變黃）的可能性，所以請事先進行确認後再使用。在加工白色或淡色布時要特别注意；

2.将本品和其他助劑拼用時，要确認好拼用助劑的性質之後，再進行預備試驗，并且跟随實際操作過程的方法來确認拼用性；

3.使用後請密封保存在陰暗處，避免陽光直射；

4.對含有本品的調整液請進行緩慢的攪拌。

貯 存

塑料桶：18公斤 保質期：12個月。

避免直射陽光，密閉保存。

Crosslinking Agent

HOLPOSON® FM-1

FM-1 is a cross-linking agent developed by Asahi Glass Co., Ltd. and can be mix-used with various fabrics to give high durability and water resistance of processed fabrics. It has multi-branch and multi-functional end blocked isocyanate group. When mix-used with water-resist agents for fabric and heated, it can improve the cross-linking effect. It has good compatibility with other weak cationic and non-ionic emulsion, such as fabric waterproofing agent. Formaldehyde will not be produced during heating treatment.

Physical & chemical properties:

Appearance: White to yellowish emulsion

Composition: End blocked isocyanate

Ionicity: Weak cationic

pH value: Weak acidic

Solubility: Soluble in water

Usage:

Padding method (Dip and roll once)

Dosage: 10-20g/L

Drying condition: 110 ℃ x 1-2 minutes

Baking condition: 170 ℃ x 1-2 minutes

Attentions:

1. There is the possibility of color change (yellowing) due to different treatment conditions. So please confirm before using. When processing white or light colored cloth, pay special attention.

2. When the product is combined with other auxiliaries, the properties of the auxiliaries should be confirmed before preliminary tests. And follow the actual operation process to confirm the compatibility.

3. Please seal and store in a dark place after use. Avoid direct sunlight.

4. Please stir the solution containing this product slowly.

Storage:

Plastic bucket: 18kg

Storage time: 12 months

Avoid direct sunlight. Store it after sealing.